silica

• シリカ

関

cristobalite、sand、silicon dioxide

　 　

WordNet

1. a white or colorless vitreous insoluble solid (SiO2); various forms occur widely in the earths crust as quartz or cristobalite or tridymite or lechatelierite (同)silicon oxide, silicon_dioxide
2. a loose material consisting of grains of rock or coral
3. a white mineral consisting of silica; found in volcanic rocks
4. a Roman building used for public administration (同)Roman basilica
5. an early Christian church designed like a Roman basilica; or a Roman Catholic church or cathedral accorded certain privileges; "the church was raised to the rank of basilica"
6. of or relating to or resembling a basilica

PrepTutorEJDIC

1. 無水ケイ酸,ケイ土
2. 〈U〉『砂』 / 《複数形で》砂地,砂浜,砂漠 / 《複数形で》時刻,時間 / …‘を'砂(紙やすり)で磨く《+『down』+『名,』+『名』+『down』》 / 〈道路など〉‘に'砂をまく
3. バシリカ(古代ローマで裁判や集会に用いられた長方形の建物) / (キリスト教の初期・中期の)バシリカ風の教会堂

Wikipedia preview

出典(authority):フリー百科事典『ウィキペディア（Wikipedia）』「2014/01/14 19:01:04」(JST)

wiki en

[Wiki en表示]

"Silica" redirects here. For other uses, see Silica (disambiguation).

Silicon dioxide
Pure silicon dioxide
IUPAC name Silicon dioxide
Other names Quartz Silica Silicic oxide Silicon(IV) oxide Crystalline silica
Identifiers
CAS number	7631-86-9 Y
PubChem	24261
ChemSpider	22683 Y
UNII	ETJ7Z6XBU4 Y
EC number	231-545-4
KEGG	C16459 N
MeSH	Silicon+dioxide
ChEBI	CHEBI:30563 Y
RTECS number	VV7565000
Gmelin Reference	200274
Jmol-3D images	Image 1
SMILES O=[Si]=O
InChI InChI=1S/O2Si/c1-3-2 Y Key: VYPSYNLAJGMNEJ-UHFFFAOYSA-N Y
Properties
Molecular formula	SiO2
Molar mass	60.08 g/mol
Appearance	Transparent crystals
Density	2.648 g·cm−3
Melting point	1,600 to 1,725 °C; 2,910 to 3,137 °F; 1,870 to 1,998 K
Boiling point	2,230 °C; 4,050 °F; 2,500 K
Related compounds
Related diones	Carbon dioxide Germanium dioxide Lead dioxide Tin dioxide
Related compounds	Silicon monoxide Silicon sulfide
Thermochemistry
Std enthalpy of formation ΔfHo298	−911 kJ·mol−1
Standard molar entropy So298	42 J·mol−1·K−1
N (verify) (what is: Y/N?) Except where noted otherwise, data are given for materials in their standard state (at 25 °C (77 °F), 100 kPa)
Infobox references

Silicon dioxide, also known as silica (from the Latin silex), is a chemical compound that is a dioxide of silicon with the chemical formula SiO₂. It has been known since ancient times. Silica is most commonly found in nature as quartz, as well as in various living organisms, Silica is one of the most complex and most abundant families of materials, existing both as several minerals and being produced synthetically. Notable examples include fused quartz, crystal, fumed silica, silica gel, and aerogels. Applications range from structural materials to microelectronics to components used in the food industry.

Production

Silicon dioxide is obtained by mining and purification of the resulting mineral. Quartz comprises more than 10% by mass of the earth's crust. It is also produced, almost always via the processing of quartz, synthetically on a very large scale.

Fumed silica

Main article: Fumed silica

Pyrogenic silica (sometimes called fumed silica or silica fume) is a very fine particulate or colloidal form of silicon dioxide. It is prepared by burning SiCl₄ in an oxygen rich hydrocarbon flame to produce a "smoke" of SiO₂.

SiCl₄ + 2 H₂ + O₂ → SiO₂ + 4 HCl.

Precipitated silica

Main article: Precipitated silica

Amorphous silica, silica gel, is produced by the acidification of solutions of sodium silicate. An initially formed gelatinous precipitate is then washed and then dehydrated to produce colorless microporous silica. Ideallized equation involving a trisilicate and sulfuric acid is shown:

Na₂Si₃O₇ + H₂SO₄ → 3 SiO₂ + Na₂SO₄ + H₂O

Approximately one billion kilograms/year (1999) of silica was produced in this manner, mainly for use for polymer composites - tires and shoe soles.

On microchips

Thin films of silica grow spontaneously on silicon wafers via thermal oxidation. This route gives a very shallow layer (approximately 1 nm or 10 Å) of so-called native oxide. Higher temperatures and alternative environments are used to grow well-controlled layers of silicon dioxide on silicon, for example at temperatures between 600 and 1200 °C, using so-called dry or wet oxidation with O₂ or H₂O, respectively. The depth of the layer of silicon replaced by the dioxide is 44% of the depth of the silicon dioxide layer produced.

The native oxide layer can be beneficial in microelectronics, where it acts as electric insulators with high chemical stability. In electrical applications, it can protect the silicon, store charge, block current, and even act as a controlled pathway to limit current flow.

Laboratory or specialty methods

From silicate esters

Many routes to silicon dioxide start with silicate esters, the best known being tetraethyl orthosilicate (TEOS). Simply heating TEOS at 680–730 °C gives the dioxide:

Si(OC₂H₅)₄ → SiO₂ + 2 O(C₂H₅)₂

Similarly TEOS combusts around 400 °C:

Si(OC₂H₅)₄ + 12 O₂ → SiO₂ + 10 H₂O + 8 CO₂

TEOS undergoes hydrolysis via the so-called sol-gel process. The course of the reaction and nature of the product are affected by catalysts, but the idealized equation is:

Si(OC₂H₅)₄ + 2 H₂O → SiO₂ + 4 HOCH₂CH₃

Other methods

Being highly stable, silicon dioxide arises from many methods. Conceptually simple, but of little practical value, combustion of silane give silicon dioxide. This reaction is analogous to the combustion of methane:

SiH₄ + 2 O₂ → SiO₂ + 2 H₂O.

Uses

An estimated 95% of silicon dioxide produced is consumed in the construction industry, e.g. for the production of Portland cement. Other major applications are listed below.

Precursor to glass and silicon metal

Silica is used primarily in the production of glass for windows, drinking glasses, beverage bottles, and many other uses. The majority of optical fibers for telecommunication are also made from silica. It is a primary raw material for many ceramics such as earthenware, stoneware, and porcelain.

Silicon dioxide is used to produce elemental silicon. The process involves carbothermic reduction in an electric arc furnace:

SiO₂ + 2 C → Si + 2 CO

Food and pharmaceutical applications

Silica is a common additive in the production of foods, where it is used primarily as a flow agent in powdered foods, or to absorb water in hygroscopic applications. It is the primary component of diatomaceous earth. Colloidal silica is also used as a wine, beer, and juice fining agent.

In pharmaceutical products, silica aids powder flow when tablets are formed.

Other

A silica-based aerogel was used in the Stardust spacecraft to collect extraterrestrial particles. Silica is also used in the extraction of DNA and RNA due to its ability to bind to the nucleic acids under the presence of chaotropes. As hydrophobic silica it is used as a defoamer component. In hydrated form, it is used in toothpaste as a hard abrasive to remove tooth plaque.

In its capacity as a refractory, it is useful in fiber form as a high-temperature thermal protection fabric. In cosmetics, it is useful for its light-diffusing properties and natural absorbency. It is also used as a thermal enhancement compound in ground source heat pump industry.

Structure

Structural motif found in α-quartz, but also found in almost all forms of silicon dioxide.

In the majority of silicates, the Si atom shows tetrahedral coordination, with 4 oxygen atoms surrounding a central Si atom. The most common example is seen in the quartz crystalline form of silica SiO₂. In each of the most thermodynamically stable crystalline forms of silica, on average, all 4 of the vertices (or oxygen atoms) of the SiO₄ tetrahedra are shared with others, yielding the net chemical formula: SiO₂.

Relation between refractive index and density for some SiO₂ forms.

For example, in the unit cell of α-quartz, the central tetrahedron shares all 4 of its corner O atoms, the 2 face-centered tetrahedra share 2 of their corner O atoms, and the 4 edge-centered tetrahedra share just one of their O atoms with other SiO₄ tetrahedra. This leaves a net average of 12 out of 24 total vertices for that portion of the 7 SiO₄ tetrahedra that are considered to be a part of the unit cell for silica (see 3-D Unit Cell).

SiO₂ has a number of distinct crystalline forms (polymorphs) in addition to amorphous forms. With the exception of stishovite and fibrous silica, all of the crystalline forms involve tetrahedral SiO₄ units linked together by shared vertices in different arrangements. Silicon–oxygen bond lengths vary between the different crystal forms, for example in α-quartz the bond length is 161 pm, whereas in α-tridymite it is in the range 154–171 pm. The Si-O-Si angle also varies between a low value of 140° in α-tridymite, up to 180° in β-tridymite. In α-quartz the Si-O-Si angle is 144°.

Fibrous silica has a structure similar to that of SiS₂ with chains of edge-sharing SiO₄ tetrahedra. Stishovite, the higher pressure form, in contrast has a rutile like structure where silicon is 6 coordinate. The density of stishovite is 4.287 g/cm³, which compares to α-quartz, the densest of the low pressure forms, which has a density of 2.648 g/cm³. The difference in density can be ascribed to the increase in coordination as the six shortest Si-O bond lengths in stishovite (four Si-O bond lengths of 176 pm and two others of 181 pm) are greater than the Si-O bond length (161 pm) in α-quartz. The change in the coordination increases the ionicity of the Si-O bond. But more important is the observation that any deviations from these standard parameters constitute microstructural differences or variations, which represent an approach to an amorphous, vitreous or glassy solid.

The only stable form under normal conditions is α-quartz and this is the form in which crystalline silicon dioxide is usually encountered. In nature impurities in crystalline α-quartz can give rise to colors (see list). The high temperature minerals, cristobalite and tridymite, have both a lower density and index of refraction than quartz. Since the composition is identical, the reason for the discrepancies must be in the increased spacing in the high temperature minerals. As is common with many substances, the higher the temperature the farther apart the atoms due to the increased vibration energy.

The high pressure minerals, seifertite, stishovite, and coesite, on the other hand, have a higher density and index of refraction when compared to quartz. This is probably due to the intense compression of the atoms that must occur during their formation, resulting in a more condensed structure.

Faujasite silica is another form of crystalline silica. It is obtained by dealumination of a low-sodium, ultra-stable Y zeolite with a combined acid and thermal treatment. The resulting product contains over 99% silica, has high crystallinity and high surface area (over 800 m²/g). Faujasite-silica has very high thermal and acid stability. For example, it maintains a high degree of long-range molecular order (or crystallinity) even after boiling in concentrated hydrochloric acid.

Molten silica exhibits several peculiar physical characteristics that are similar to the ones observed in liquid water: negative temperature expansion, density maximum (at temperatures ~5000 °C), and a heat capacity minimum. Its density decreases from 2.08 g/cm³ at 1950 °C to 2.03 g/cm³ at 2200 °C. When molecular silicon monoxide, SiO, is condensed in an argon matrix cooled with helium along with oxygen atoms generated by microwave discharge, molecular SiO₂ is produced with a linear structure. Dimeric silicon dioxide, (SiO₂)₂ has been prepared by reacting O₂ with matrix isolated dimeric silicon monoxide, (Si₂O₂). In dimeric silicon dioxide there are two oxygen atoms bridging between the silicon atoms with an Si-O-Si angle of 94° and bond length of 164.6 pm and the terminal Si-O bond length is 150.2 pm. The Si-O bond length is 148.3 pm, which compares with the length of 161 pm in α-quartz. The bond energy is estimated at 621.7 kJ/mol.

Fused quartz

Main article: Fused quartz

When molten silicon dioxide SiO₂ is rapidly cooled, it does not crystallize but solidifies as a glass. The geometry of the silicon and oxygen centers in glass is similar to that in quartz and most other crystalline forms of the same composition, i.e., silicon is surrounded by a regular tetrahedra of oxygen centers. The difference between the glass and the crystalline forms arise from the connectivity of these tetrahedral units. Although there is no long range periodicity in the glassy network there remains significant ordering at length scales well beyond the SiO bond length. One example of this ordering is found in the preference of the network to form rings of 6-tetrahedra.

The glass transition temperature of pure SiO₂ is about 1475 K.

Chemical reactions

Manufactured silica fume at maximum surface area of 380 m²/g

Silica is converted to silicon by reduction with carbon.

Fluorine reacts with silicon dioxide to form SiF₄ and O₂ whereas the other halogen gases (Cl₂, Br₂, I₂) are essentially unreactive.

Silicon dioxide is attacked by hydrofluoric acid (HF) to produce hexafluorosilicic acid:

SiO₂ + 6 HF → H₂SiF₆ + 2 H₂O.

HF is used to remove or pattern silicon dioxide in the semiconductor industry.

Silicon dioxide dissolves in hot concentrated alkali or fused hydroxide, as described in this idealized equation:

SiO₂ + 2 NaOH → Na₂SiO₃ + H₂O.

Silicon dioxide reacts with basic metal oxides (e.g. sodium oxide, potassium oxide, lead(II) oxide, zinc oxide, or mixtures of oxides forming silicates and glasses as the Si-O-Si bonds in silica are broken successively). As an example the reaction of sodium oxide and SiO₂ can produce sodium orthosilicate, sodium silicate, and glasses, dependent on the proportions of reactants:

2 Na₂O + SiO₂ → Na₄SiO₄;

Na₂O + SiO₂ → Na₂SiO₃;

(0.25–0.8)Na₂O + SiO₂ → glass.

Examples of such glasses have commercial significance, e.g. soda-lime glass, borosilicate glass, lead glass. In these glasses, silica is termed the network former or lattice former.

Bundle of optical fibers composed of high purity silica.

Silicon dioxide reacts with elemental silicon at high temperatures to produce SiO:

SiO₂ + Si → 2 SiO

Solubility in water

The solubility of silicon dioxide in water strongly depends on its crystalline form and is 3–4 times higher for silica than quartz; as a function of temperature, it peaks at about 340 °C. This property is used to grow single crystals of quartz in a hydrothermal process where natural quartz is dissolved in superheated water in a pressure vessel that is cooler at the top. Crystals of 0.5–1 kg can be grown over a period of 1–2 months. These crystals are a source of very pure quartz for use in electronic applications.

Occurrence

Biology

Even though it is poorly soluble, silica occurs widely in many plants. Plant materials with high silica phytolith content appear to be of importance to grazing animals, from chewing insects to ungulates. Studies have shown that it accelerates tooth wear, and high levels of silica in plants frequently eaten by herbivores may have developed as a defense mechanism against predation.

It is also the primary component of rice husk ash, which is used, for example, in filtration and cement manufacturing.

Silicification in and by cells has been common in the biological world for well over a billion years. In the modern world it occurs in bacteria, single-celled organisms, plants, and animals (invertebrates and vertebrates). Prominent examples include:

• Tests or frustules of diatoms and Radiolaria.
• Silica phytoliths in the cells of many plants, including Equisetaceae, practically all grasses, and a wide range of dicotyledons.
• The spicules forming the skeleton of many sponges.

Crystalline minerals formed in the physiological environment often show exceptional physical properties (e.g. strength, hardness, fracture toughness) and tend to form hierarchical structures that exhibit microstructural order over a range of scales. The minerals are crystallized from an environment that is undersaturated with respect to silicon, and under conditions of neutral pH and low temperature (0–40 °C).

Formation of the mineral may occur either within the cell wall of an organism (such as with phytoliths), or outside the cell wall, as typically happens with tests. Specific biochemical reactions exist for mineral deposition. Such reactions include those that involve lipids, proteins, and carbohydrates.

It is unclear in what ways silica is important in the nutrition of animal. This field of research is challenging because silica is ubiquitous and in most circumstances dissolves in trace quantities only. All the same it certainly does occur in the living body, leaving us with the problem that it is hard to create proper silica-free controls for purposes of research. This makes it difficult to be sure when the silica present has had operative beneficial effects, and when its presence is coincidental, or even harmful. The current consensus is that it certainly seems important in the growth, strength, and management of many connective tissues. This is true not only for hard connective tissues such as bone and tooth but possibly in the biochemistry of the subcellular enzyme-containing structures as well.

Health effects

Quartz sand (silica) as main raw material for commercial glass production

Silica ingested orally is essentially nontoxic, with an LD50 of 5000 mg/kg. On the other hand, inhaling finely divided crystalline silica dust can lead to silicosis, bronchitis, or cancer, as the dust becomes lodged in the lungs and continuously irritates them, reducing lung capacities. Prior to new rules issued in 2013 OSHA allowed 100 micrograms a cubic meter of air. The new regulations reduce the amount to 50 µg/m³ down from 100 µg/m³. The exposure limit for the construction industry is also set at 50 µg/m³ down from 250 µg/m³.

In the body crystalline silica particles do not dissolve over clinically relevant periods. Silica crystals can activate the NLRP3 inflammasome inside macrophages and dendritic cells and thereby result in processing of pro-Interleukin 1 beta into its mature form. Chronic exposure to silica may thereby account for some of its health hazards, as interleukin-1 is a highly pro-inflammatory cytokine in the immune system. This effect can create an occupational hazard for people working with sandblasting equipment, products that contain powdered crystalline silica and so on. Children, asthmatics of any age, allergy sufferers, and the elderly (all of whom have reduced lung capacity) can be affected in much less time. Amorphous silica, such as fumed silica is not associated with development of silicosis, but may cause irreversible lung damage in some cases. Laws restricting silica exposure with respect to the silicosis hazard specify that they are concerned only with silica that is both crystalline and dust-forming.

A study that followed subjects for 15 years found that higher levels of silica in water appeared to decrease the risk of dementia. The study found an association between an increase of 10 milligram-per-day of the intake of silica in drinking water with a decreased risk of dementia of 11%.

Crystalline silica is used in hydraulic fracturing of formation which contain tight oil and shale gas, a use which presents a health hazard to workers. In 2013 OSHA announced tightened restrictions on the amount of crystalline silica which could be present and required "green completion" of fracked wells to reduce exposure during the initial burst of material emitted by a fracked well.

Crystalline forms of silicon dioxide

SiO₂, more so than almost any material, exists in many crystalline forms (called polymorphs).

Crystalline forms of SiO₂

Form	Crystal symmetry Pearson symbol, group No.	ρ g/cm3	Notes	Structure
α-quartz	rhombohedral (trigonal) hP9, P3121 No.152	2.648	Helical chains making individual single crystals optically active; α-quartz converts to β-quartz at 846 K
β-quartz	hexagonal hP18, P6222, No. 180	2.533	closely related to α-quartz (with an Si-O-Si angle of 155°) and optically active; β-quartz converts to β-tridymite at 1140 K
α-tridymite	orthorhombic oS24, C2221, No.20	2.265	metastable form under normal pressure
β-tridymite	hexagonal hP12, P63/mmc, No. 194		closely related to α-tridymite; β-tridymite converts to β-cristobalite at 2010 K
α-cristobalite	tetragonal tP12, P41212, No. 92	2.334	metastable form under normal pressure
β-cristobalite	cubic cF104, Fd3m, No.227		closely related to α-cristobalite; melts at 1978 K
faujasite	cubic cF576, Fd3m, No.227	1.92	sodalite cages connected by hexagonal prisms; 12-membered ring pore opening; faujasite structure.
melanophlogite	cubic (cP*, P4232, No.208) or tetragonal (P42/nbc)	2.04	Si5O10, Si6O12 rings; mineral always found with hydrocarbons in interstitial spaces-a clathrasil
keatite	tetragonal tP36, P41212, No. 92	3.011	Si5O10, Si4O14, Si8O16 rings; synthesised from glassy silica and alkali at 600–900 K and 40–400 MPa
moganite	monoclinic mS46, C2/c, No.15		Si4O8 and Si6O12 rings
coesite	monoclinic mS48, C2/c, No.15	2.911	Si4O8 and Si8O16 rings; 900 K and 3–3.5 GPa
stishovite	Tetragonal tP6, P42/mnm, No.136	4.287	One of the densest (together with seifertite) polymorphs of silica; rutile-like with 6-fold coordinated Si; 7.5–8.5 GPa
fibrous W-silica	orthorhombic oI12, Ibam, No.72	1.97	like SiS2 consisting of edge sharing chains, melts at ~1700 K
seifertite	orthorhombic oP, Pbcn	4.294	One of the densest (together with stishovite) polymorphs of silica; is produced at pressures above 40 GPa.

See also

• Fused quartz
• Mesoporous silica
• Thermal oxidation
• Silicon carbide

References

External links

• Tridymite, International Chemical Safety Card 0807
• Quartz, International Chemical Safety Card 0808
• Cristobalite, International Chemical Safety Card 0809
• amorphous, NIOSH Pocket Guide to Chemical Hazards
• crystalline, as respirable dust, NIOSH Pocket Guide to Chemical Hazards
• Formation of silicon oxide layers in the semiconductor industry. LPCVD and PECVD method in comparison. Stress prevention.
• Quartz SiO₂ piezoelectric properties
• Silica (SiO₂) and Water
• Epidemiological evidence on the carcinogenicity of silica: factors in scientific judgement by C. Soutar and others. Institute of Occupational Medicine Research Report TM/97/09
• Scientific opinion on the health effects of airborne silica by A Pilkington and others. Institute of Occupational Medicine Research Report TM/95/08
• The toxic effects of silica by A Seaton and others. Institute of Occupational Medicine Research Report TM/87/13

Media related to Silicon dioxide at Wikimedia Commons

•  Chisholm, Hugh, ed. (1911). "Silica". Encyclopædia Britannica (11th ed.). Cambridge University Press 

UpToDate Contents

全文を閲覧するには購読必要です。 To read the full text you will need to subscribe.

• 1. 珪肺症 silicosis
• 2. 全身性硬化症（強皮症）の危険因子および考えられる原因 risk factors for and possible causes of systemic sclerosis scleroderma
• 3. 関節リウマチの疫学、危険因子、および可能性のある原因 epidemiology of risk factors for and possible causes of rheumatoid arthritis
• 4. 間質性肺疾患における肺生検結果の解釈 interpretation of lung biopsy results in interstitial lung disease
• 5. バルカン流行性腎症 balkan endemic nephropathy

English Journal

• TEM studies of zeolites and ordered mesoporous materials.

• Diaz I, Mayoral A.SourceInstituto de Catalisis y Petroleoquimica, CSIC. c/Marie Curie 2, 28049 Madrid, Spain.
• Micron (Oxford, England : 1993).2011 Jul;42(5):512-27. Epub 2010 Dec 24.
• In the present manuscript we have reviewed recent results on transmission electron microscopy of beam sensitive materials such as zeolites and ordered mesoporous materials. The results of the investigation of the fine structure of different zeolite types as MFI, ITQ-7 and the presence of mixture of
• PMID 21227705

• Evidence for a biogenic, microorganismal origin of rock varnish from the Gangdese Belt of Tibet.

• Wang X, Zeng L, Wiens M, Schlosmacher U, Jochum KP, Schroder HC, Muller WE.SourceNational Research Center for Geoanalysis, 26 Baiwanzhuang Dajie, CHN-100037 Beijing, China; Institute for Physiological Chemistry, Johannes Gutenberg University, Medical School, Duesbergweg 6, D-55099 Mainz, Germany.
• Micron (Oxford, England : 1993).2011 Jul;42(5):401-411. Epub 2010 Dec 13.
• In the present study we examined material from the Ashikule Basin of Tibet. Chemical analyses were performed by use of energy dispersive X-ray spectroscopy and electron probe microanalysis to clarify whether the varnish layers that had developed on the surface of the rhyolite are indeed composed of
• PMID 21194958

Japanese Journal

• ソフト化学的手法を用いたナノポーラス材料の合成と細孔の化学修飾 (小特集 ナノポーラス材料の新展開)

• 武井 貴弘,三浦 章,熊田 伸弘
• 表面技術 = Journal of the Surface Finishing Society of Japan 65(1), 2-6, 2014-01
• NAID 40019934868

• 長時間オートクレーブ養生が高強度モルタルの強度発現性と微細構造に及ぼす影響

• 前田 拓海,高田 卓志,佐藤 平 [他]
• Journal of the Society of Inorganic Materials, Japan : セッコウ・石灰・セメント・地球環境の科学 21(368), 15-21, 2014-01
• NAID 40019933773

• キュリー・ポイント・パイロライザーを用いた階層構造を持つYゼオライト含有メソ多孔性シリカ-アルミナ触媒によるVGOの接触分解

• 石原 篤,木村 健太郎,橋本 忠範 [他]
• Journal of the Japan Petroleum Institute 57(1), 34-46, 2014-01
• NAID 40019932132

• Photoluminescence Characteristics of Bi

• Wen Jianxiang,Wang Tingyun,Pang Fufei,Zeng Xianglong,Chen Zhenyi,Peng Gang-Ding
• Jpn J Appl Phys 52(12), 122501-122501-4, 2013-12-25
• … The energy levels associated with structural models of different valence states of Bi ions in Bi-doped silica optical fiber are investigated using the density functional theory of quantum-chemical calculation. …
• NAID 150000107840

Related Links

• SILICA - The Engineers of Distribution

SILICA (an Avnet company) offers products from 28 leading semiconductor suppliers and a full set of logistical services. We have 44 local branches Across EMEA region. ... SILICA Xynergy-M4 The SILICA Xynergy-M4 Board ...

• ガラス工房シリカ

ガラス工房 SILICA 北茨城市が一望できる茜平にあります。 ガラスを体験し、見学し、皆さんにガラスを知ってもらう施設です。 ガラスの原料は、大部分が硅砂（シリカサンド）から出来ています。 SILICAの名は、ここから ...

• 株式会社 東日本シリカ

株式会社 東日本シリカは、環境配慮型製品の企画・提案及び土木・建築資材を取り扱っております。 ... 太陽光発電 PHOTOVOLTAIC POWER GENERATION 鉄塔工事・インフラ整備 無線基地局の候補地選定を的確にスピーディーに実施し ...

Related Pictures

---

★リンクテーブル★

リンク元	「sand」「cristobalite」「silicon dioxide」「シリカ」
拡張検索	「borosilicate」「magnesium silicate」「magnesii silicas」

「sand」

　　[★]

• 砂、砂地、砂漠、砂をまく

関

cristobalite、desert、silica、silicon dioxide

　 　

「cristobalite」

　　[★]

クリストバル石

関

sand、silica、silicon dioxide

　

「silicon dioxide」

　　[★]

二酸化ケイ素

関

cristobalite、sand、silica

「シリカ」

　　[★]

英

silica, silicon dioxide

関

珪肺

「borosilicate」

　　[★]

• ホウケイ酸、(化合物)ウケイ酸塩

　

「magnesium silicate」

　　[★]

ケイ酸マグネシウム

関

Florisil

「magnesii silicas」

　　[★] ケイ酸マグネシウム